KMT-8211
Uncured Properties | |
Appearance | Pellet |
CureCondition：150℃/4min + 150℃/4hr | |
Cured Properties | |
Hardness Shore D | 80 |
Transmittance（450nm/2mm） | ≥85% |
Tg | ≥120℃ |
cure shrinkage rate | ≤1.5% |
Flexural Modulus | 2.6-3.5MPa |
Flexural Strength | ≥110MPa |
Linear Expansion Coefficientα1 | 60-100ppm |
Linear Expansion Coefficientα2 | 150-190ppm |
(Specific Gravity)25℃ | 1.25-1.30g/cm3 |
Note：
ü These are all experimental data and had been measured under the test condition of 25 degrees Celsius ,Please confirm through the experiment if it`s fit for use.
ü Product performance can be adjusted according to the customer reques